# SAE10v45 Cold Drawn 29% from HotRolled 33mm diam. bar, HRc= 32 # Constant Ampl. Tests, axial specimens # Chem.: 0.44wt%C .87Mn .025S .016P .26Si .08Cu .18Cr .02Mo .05Ni # .12V .023Al .013N # Paper contains dislocation cell size information. # Ref.: W.Dowling, jr., W.Donlon, "The Effect of Cold Work on # the Fatigue Behavior of 10v45," Book: Microalloyed Bar and # Forging Steels," Ed. C.J.Van Tyne Krauss, Matlock, # The Minerals Metals + Matls Soc. 1996, pg.507-515. # Warning: Data digitized from graphs, may contain errors # Tested by RuiXian Yu UWaterloo 1996 #FileType= strain_life #DataType= raw #Name= SAE10v45 #Name= ColdDraw29% #Stress_units= mpa #Strain_units= strain #Sy= 1010 mpa #Su= 0. #E= 209300 #RA= 0. #TrueFractureStrain= 0. #TrueFractureStress= 0 #monotonic_K= .0 #monotonic_n= 0. #BHN= 279 #TotStrAmpl 2Nf StsAmpl So PlasStrAmpl ElasticModulus 0.00764 4216 712 0 0.00424 209300 0.00606 8189 686 0 0.00278 209300 0.00510 14414 676 0 0.00186 209300 0.00422 26067 653 0 0.00110 209300 0.00344 41835 652 0 0.00032 209300 0.00317 81040 633 0 0.00014 209300 0.00291 151210 616 0 0.00000 209300 0.00275 265360 577 0 0.00000 209300 0.00259 896350 557 0 0.00000 209300 0.00245 1976750 527 0 0.00000 209300 0.00229 8651500 501 0 0.00000 209300 0.00216 21760000 456 0 0.00000 209300 #runout # #