# SAE10v45 Cold Drawn 18% from HotRolled 33mm diam. bar, HRc= 29 # Constant Ampl. Tests, axial specimens # Chem.: 0.44wt%C .87Mn .025S .016P .26Si .08Cu .18Cr .02Mo .05Ni # .12V .023Al .013N # Paper contains dislocation cell size information. # Ref.: W.Dowling, jr., W.Donlon, "The Effect of Cold Work on # the Fatigue Behavior of 10v45," Book: Microalloyed Bar and # Forging Steels," Ed. C.J.Van Tyne Krauss, Matlock, # The Minerals Metals + Matls Soc. 1996, pg.507-515. # Warning: Data digitized from graphs, may contain errors # Tested by RuiXian Yu UWaterloo 1996 #FileType= strain_life #DataType= raw #Name= SAE10v45 #Name= ColdDraw18% #Stress_units= mpa #Strain_units= strain #Sy= 890 mpa #Su= 0. #E= 213800 #RA= 0. #TrueFractureStrain= 0. #TrueFractureStress= 0 #monotonic_K= .0 #monotonic_n= 0. #BHN= 279 #TotStrAmpl 2Nf StsAmpl So PlasStrAmpl ElasticModulus 0.00855 3782 699 0 0.00528 213800 0.00700 5351 668 0 0.00388 213800 0.00589 8736 635 0 0.00292 213800 0.00492 9001 602 0 0.00210 213800 0.00433 15524 585 0 0.00159 213800 0.00361 15725 576 0 0.00091 213800 0.00372 43450 569 0 0.00106 213800 0.00351 61720 572 0 0.00083 213800 0.00301 67625 559 0 0.00039 213800 0.00351 71470 587 0 0.00077 213800 0.00270 150130 537 0 0.00019 213800 0.00241 476800 508 0 0.00004 213800 0.00221 15712500 466 0 0.00004 213800 0.00211 16089000 439 0 0.00006 213800 0.00202 23971500 432 0 0.00000 213800 #runout # #