# SAE10v45 Hot Rolled 33mm diam. bar, HRc= 20 
# Constant Ampl. Tests, axial specimens  
# Chem.: 0.44wt%C .87Mn .025S .016P .26Si .08Cu .18Cr .02Mo .05Ni
# .12V .023Al .013N 
# Paper contains dislocation cell size information.
# Ref.: W.Dowling, jr., W.Donlon, "The Effect of Cold Work on 
# the Fatigue Behavior of 10v45," Book: Microalloyed Bar and 
# Forging Steels," Ed. C.J.Van Tyne Krauss, Matlock, 
# The Minerals Metals + Matls Soc. 1996, pg.507-515.
# Warning: Data digitized from graphs, may contain errors
# Tested by  RuiXian Yu UWaterloo 1996

#FileType= strain_life
#DataType= raw
#Name= SAE10v45
#Name= HotRolled
#Stress_units= mpa
#Strain_units= strain
#Sy= 570 mpa   
#Su= 0.
#E= 204500
#RA= 0.
#TrueFractureStrain= 0.
#TrueFractureStress= 0
#monotonic_K= .0
#monotonic_n= 0.
#BHN= 226 

#TotStrAmpl 2Nf StsAmpl So PlasStrAmpl ElasticModulus
0.00807  4007  661  0  0.00483  204500
0.00693  5670  622  0  0.00389  204500
0.00603  11131  572  0  0.00323  204500
0.00502  15695  567  0  0.00224  204500
0.00404  25016  540  0  0.00140  204500
0.00350  43290  489  0  0.00111  204500
0.00301  63815  489  0  0.00062  204500
0.00270  212605  463  0  0.00044  204500
0.00251  437900  435  0  0.00038  204500
0.00221  1110550  421  0  0.00015  204500
0.00231  1197400  413  0  0.00029  204500
0.00211  1534800  409  0  0.00011  204500
0.00201  4877000  389  0  0.00010  204500
0.00180  20344000  363  0  0.00002  204500 #runout
#
#