#Copyright (C) 2011 F.A.Conle #This data file is free software - you can redistribute it and/or #modify it under the terms of the GNU General Public License as #published by the Free Software Foundation; either version 2 of the #license, or (at your option) any later version. #This data file is distributed in the hope that it will be useful, #but WITHOUT ANY WARRANTY - without even the implied warranty of #MERCHANTABILITY or FITNESS FOR A PARTICULAR PURPOSE. See the #GNU General PUblic License for more details. #You should have received a copy of the GNU General PUblic License #along with this program - if not, write to the Free Software #Foundation, Inc., 59 Temple Place - Suite 330, Boston, MA 02111-1307, USA #Try also their web site: http://www.gnu.org/copyleft/gpl.html # # SAE1038 Fully Annealed, # 0.39wt%C .35Si .75Mn .019P .009S .19Cr .13Ni .21Cu .03Sn .02Pb # Ref.: M.Schwartz + J.C.Crespi, "Fracture of Pearlite under Conditions # of High Deformation Fatigue," ASTM STP 942, 1988, pp.77-93. # # Note: Data may contain errors from digitization process. # #FileType= strain_life #DataType= raw #TIMEcol= 0 #NAME= SAE1038 #NAME= FullAnnealed #NAME= Steel #Stress_units= mpa #Strain_units= strain #Su= 610. mpa #Sy= 347. mpa #E= 207000. #FractureStrain= 0.59 #FractureStress= 976. #BHN= 0. #RA= 55.5 % #monotonic_n= 0.23 #monotonic_K= 994 mpa #digitzation file sae1038Schwartz-Crespi.ods #StrAmpl 2Nf StsAmpl So PlasStrAmpl IniMod 0.02078 360 702 0 0.01739 207000 0.02074 394 662 0 0.01754 207000 0.02073 414 661 0 0.01753 207000 0.01883 564 688 0 0.01550 207000 0.01859 617 628 0 0.01555 207000 0.01660 621 664 0 0.01338 207000 0.01457 848 521 0 0.01205 207000 0.01439 898 576 0 0.01161 207000 0.01484 1120 587 0 0.01200 207000 0.01235 1250 512 0 0.00988 207000 0.01246 1443 578 0 0.00966 207000 0.01243 1632 590 0 0.00958 207000 0.01047 1807 486 0 0.00812 207000 0.01034 1894 497 0 0.00794 207000 0.01045 2028 490 0 0.00808 207000 0.00881 3901 496 0 0.00642 207000 0.00823 3984 474 0 0.00594 207000 0.00823 4144 479 0 0.00591 207000 0.00831 4567 473 0 0.00602 207000 0.00615 6505 415 0 0.00414 207000 0.00621 6967 429 0 0.00414 207000 0.00628 7379 405 0 0.00432 207000 0.00408 26105 401 0 0.00215 207000 0.00408 27951 382 0 0.00223 207000 0.00201 134715 287 0 0.00062 207000 0.00207 169155 258 0 0.00083 207000 # #