#Copyright (C) 2019 F.D.E. Committee #This data file is free software - you can redistribute it and/or #modify it under the terms of the GNU General Public License as #published by the Free Software Foundation; either version 2 of the #license, or (at your option) any later version. #This data file is distributed in the hope that it will be useful, #but WITHOUT ANY WARRANTY - without even the implied warranty of #MERCHANTABILITY or FITNESS FOR A PARTICULAR PURPOSE. See the #GNU General PUblic License for more details. #You should have received a copy of the GNU General PUblic License #along with this program - if not, write to the Free Software #Foundation, Inc., 59 Temple Place - Suite 330, Boston, MA 02111-1307, USA #Try also their web site: http://www.gnu.org/copyleft/gpl.html # # FreeForm MicroAlloy Steel, ColdWorked 40pc. HRc=24 # A low carbon bainitic steel for Cold Forging for fasteners. # After hot rolled rod, Stelmore controlled cooling line, the Cold work 40pc. # Not Annealed after CWork. # Chem.: .11wt%C 1.56Mn .003S .011P .26Si .092Cb .025Al .0032B .01Ti .009N # Ref.: A.T.Joenoes, A.M.Gokhale, S.P.Bhat, W.E.Heitmann, "Cyclic Deformation # and Fatigue Behavior of FreeForm- a Micro-Alloyed Low Carbon Bainitic Steel # Book:"Microalloyed Bar and Forgin Steels," Eds.C.J.vanTyne et al, # The Minerals, Metals, + Metallurgy Soc. 1996 pp. 517-531. # Note: Digitized from graphs, may contain errors. # Note: 2Nf values were given as averages. #FileType= strain_life #DataType= raw #TIMEcol= 0 #Name= MicroAlloy #Name= Cb-Al-B-Ti #Name= 40pcColdWoek #stress_units= mpa #strain_units= strain #Sy= 703 mpa #Su= 862 #E= 201000. estimated. #%RA= 59. % #%Elongation= 15.6 #TrueFractureStress= 0 #TrueFractureStrain= 0 #BHN= 260 #StrAmpl 2Nf StsAmpl SoPlsStrAmp Emod 0.01244 508 633 0 0.00943 210000 0.01244 508 616 0 0.00951 210000 0.00991 924 630 0 0.00691 210000 0.01000 924 602 0 0.00713 210000 0.00785 1964 584 0 0.00507 210000 0.00787 1964 605 0 0.00499 210000 0.00798 1964 599 0 0.00512 210000 0.00870 1964 564 0 0.00602 210000 0.00489 9747 542 0 0.00231 210000 0.00287 41097 439 0 0.00077 210000 0.00288 41097 486 0 0.00057 210000 0.00292 41097 456 0 0.00075 210000 0.00194 434290 414 0 0. 210000 # #