#Copyright (C) 2014 F.D.E. Committee #This data file is free software - you can redistribute it and/or #modify it under the terms of the GNU General Public License as #published by the Free Software Foundation; either version 2 of the #license, or (at your option) any later version. #This data file is distributed in the hope that it will be useful, #but WITHOUT ANY WARRANTY - without even the implied warranty of #MERCHANTABILITY or FITNESS FOR A PARTICULAR PURPOSE. See the #GNU General PUblic License for more details. #You should have received a copy of the GNU General PUblic License #along with this program - if not, write to the Free Software #Foundation, Inc., 59 Temple Place - Suite 330, Boston, MA 02111-1307, USA #Try also their web site: http://www.gnu.org/copyleft/gpl.html # # A514 Steel # AnalysisChem: .20C .82Mn .010P .016S .24Si .08Ni .51Cr .20Mo Cu<0.01 # Ref.:F.V.Lawrence Jr., N.J.Ho, P.K.Mazumdar, U.Illinois FCP Report 36 Oct 1980. # Not checked but probably original is in: # Ref.: Y. Higashida, "Strain Controlled Fatigue Behavior of Weld Metal # and Heat-Affected Base Metal in A36 and A514 Steel Welds," Ph.D Thesis, Dept. of # Metallurgy and Mining, U. of Illinois, June 1976. # Note: Data digitized from figures. May contain errors. # #FileType= strain_life #DataType= raw #TIMEcol= 0 #NAME= ASTM-A514 #NAME= Steel #Stress_units= mpa #Strain_units= strain #Sy= 890. 0.2pc offset, 1295 ksi #Su= 938. mpa 143. ksi #eu= 0. #strain at Su not reported #E= 209000. mpa = 30300. ksi #FractureStrain= 1.0 #FractureStress= 1270 mpa = 184 ksi #monotonic_K= 1187 mpa, 172 ksi #monotonic_n= 0.060 #BHN= 303 #%RA= 63. % #Plastic strains below are = TotStrAmpl - (StsAmpl/IniMod) #StrAmpl 2Nf StsAmpl So PlasStrAmpl IniMod NeuberStressAmpl 0.01563 555 770 0 0.01195 209000 1586 0.01065 1204 726 0 0.00717 209000 1271 0.00810 1886 720 0 0.00465 209000 1104 0.00533 5244 656 0 0.00219 209000 855 0.00399 19039 595 0 0.00114 209000 704 0.00320 43228 535 0 0.00064 209000 598 0.00249 412974 469 0 0.00024 209000 494 0.00192 7440590 389 0 0.00006 209000 395 #runout # #