#NAME= SAE1015
#NAME= Mild_Steel
#NAME= Normalized
#Digitized data from graph in PhD Thesis:
#S.Keshavan, "Some Studies on the Deformation and Fracture of 
#             Normalized Mild Steel under Cyclic Conditions,"
#            PhD Thesis, Univ. of Waterloo, Dec. 1967 p37.
#digitized zero= 1.46E-03   0.14
#Strain_units= strain
#Stress_units= ksi
#gaugelength= 0.30 inches
#
#E= 30000.   #ksi
#%RA= 67.8 #%
#TrueFractureStrain= 1.136
#TrueFractureStress= 105.3 #ksi
#Test Duration = 3 minutes.
#Ramberg Osgood in Strain hardening region = TrueStress= 99.5 * (TrueStrain**0.26)
#Chem= .143C .47Mn .025S .004Phos .037Si 0.Ni .01Cr 0.Mo
#BHN= 80 # Rockwell Superf. 1/16in ball, 30kg measured as = 47
#TEMP= 21 #Room Temp.
#Material supplied by Stelco Steel, in the form of semi-killed
#hot-rolled 2.5in X 1.25in bar stock. Steel was normalised by soaking
# at 1600F for 30min and then cooled in air.  Specimens were machined
# from near center of bar; 0.375in long, 0.20in diam. test section
#

Note: Above data only good to ultimate.

Note: Above data only good to ultimate.

   
ABAQUS Compatible Data:
*MATERIAL,NAME=sae1015normalized
*ELASTIC
  206000., 0.30
*PLASTIC
    0., 0.000000,
  293., 0.000000,
  226., 0.000320,
  226., 0.000120,
  228., 0.008850,
  280., 0.025380,
  363., 0.056320,
  392., 0.078020,
  440., 0.126270,
  469., 0.159850,
  513., 0.217460,
  528., 0.239610,
  557., 0.283990,
#Data below is past the ultimate, only true frac SS is last point
#  568., 0.305480,
#  578., 0.337240,
#  577., 0.369460,
#  561., 0.395390,
#  547., 0.410130,
#  497., 0.427430,
#  429., 0.443250,
#True Fracture stress strain:
   726., 1.136
#