#Copyright (C) 2014 F.D.E. Committee #This data file is free software - you can redistribute it and/or #modify it under the terms of the GNU General Public License as #published by the Free Software Foundation; either version 2 of the #license, or (at your option) any later version. #This data file is distributed in the hope that it will be useful, #but WITHOUT ANY WARRANTY - without even the implied warranty of #MERCHANTABILITY or FITNESS FOR A PARTICULAR PURPOSE. See the #GNU General PUblic License for more details. #You should have received a copy of the GNU General PUblic License #along with this program - if not, write to the Free Software #Foundation, Inc., 59 Temple Place - Suite 330, Boston, MA 02111-1307, USA #Try also their web site: http://www.gnu.org/copyleft/gpl.html # # QStE420 HSLA-060XLK S420MC steel HotRolled sheet # Specimens 10.5mm gauge length, 4mm wide, 3mm thick. # Ref. L.DePrada, C.Maestro, J.Romo, E.Canibano, J.C.Merino, "Fatigue # Behaviour of High Strength Steel Sheets Used in Automotive Industry," # Fatigue 2007. # Data points digitzed from graphs and may contain errors. # #FileType= strain_life #DataType= raw #TIMEcol= 0 #NAME= QStE420 #NAME= HSLA-060XLK #NAME= SteelSheet #Strain_units= strain #Stress_units= mpa #Sy= 529. mpa #Su= 572. #eu= 0.0 # Strain at Ultimate not reported #Elongation 28.7% reported #E= 191000 mpa #%RA= 68.8 % #BHN= 0. not reported #FractureStrain= 1.16 not reported, compute from %RA #FractureStress= 0. not reported #monotonic_K= 0 not reported #monotonic_n= 0 not reported #TotStrAmpl 2Nf StsAmpl So PlasStrAmpl InitModulus NeubEqStsAmp 0.00407 8272 449 0 0.00172 191000 590 0.00407 9152 456 0 0.00168 191000 595 0.00404 9917 464 0 0.00161 191000 598 0.00360 14259 441 0 0.00129 191000 551 0.00358 15353 440 0 0.00128 191000 548 0.00357 16393 440 0 0.00127 191000 548 0.00305 19662 416 0 0.00087 191000 492 0.00307 21231 423 0 0.00085 191000 498 0.00255 46091 391 0 0.00050 191000 436 0.00253 55252 388 0 0.00050 191000 433 0.00230 77811 384 0 0.00029 191000 411 0.00207 81454 358 0 0.00019 191000 376 0.00205 107675 353 0 0.00020 191000 372 0.00202 140875 348 0 0.00020 191000 366 0.00179 259535 322 0 0.00010 191000 331 0.00181 420105 327 0 0.00010 191000 336 0.00154 2382270 293 0 0.00000 191000 293 # #