#Copyright (C) 2012 F.D.E. Committee #This data file is free software - you can redistribute it and/or #modify it under the terms of the GNU General Public License as #published by the Free Software Foundation; either version 2 of the #license, or (at your option) any later version. #This data file is distributed in the hope that it will be useful, #but WITHOUT ANY WARRANTY - without even the implied warranty of #MERCHANTABILITY or FITNESS FOR A PARTICULAR PURPOSE. See the #GNU General PUblic License for more details. #You should have received a copy of the GNU General PUblic License #along with this program - if not, write to the Free Software #Foundation, Inc., 59 Temple Place - Suite 330, Boston, MA 02111-1307, USA #Try also their web site: http://www.gnu.org/copyleft/gpl.html # # 13Cr4Ni Stainless Steel, AISI-415 from forged bars, then heat treated: # Austenized 985C 1hr, oil quenched, Tempered 600C 4hr, air cooled # .037C wt% .21Si .53Mn 4.19Ni 12.71Cr .66Mo # Note: File contains both Axial and Rotating Bending data. # also both transverse and longitudinal direction, as noted below. # Ref.: D.Wagner, J.-P. Chavaillard, Y.Meyzaud, M.Bonningue, R.Cozar # and G.Baudry, "Toughness and Fatigue Properties of Matensitic # Stainless Steels for Nuclear Applications," Matls. for Energy Systems, # V.6, N4, March 1985 pp.263-272. # Data digitized from graphs and may contain errors. # #FileType= strain_life #DataType= raw #TIMEcol= 0 #NAME= SS-13Cr4Ni #NAME= AISI-415 #Name= unaged #NAME= StainlessSteel #Stress_units= mpa #Strain_units= strain #Sy= 712. Longt.=720, Tranv.=704 #Su= 800. #eu= 0 #strain at Su not reported #E= 201000. mpa =29170 ksi (taken from ASME documents) #FractureStrain= .0 not reported #FractureStress= 0. not reported #monotonic_K= 0 not reported #monotonic_n= 0 not reported #BHN= 0. #%RA= 0. % #StrAmpl 2Nf StsAmpl So PlasStrAmpl IniMod NeuberStressAmpl 0.015 408 718 0 0.01143 201000 1471 0.015 519 718 0 0.01143 201000 1471 0.01 1084 672 0 0.00666 201000 1162 0.01 1904 672 0 0.00666 201000 1162 0.005 11242 611 0 0.00196 201000 784 0.005 13423 611 0 0.00196 201000 784 0.0029 78844 556 0 0.00013 201000 569 0.0029 65021 556 0 0.00013 201000 569 #Above data are axial test results. #Rotating bending data below. #Unaged specimens, Transverse 0.00273 383553 549 0 0 201000 549 0.00263 321342 529 0 0 201000 529 0.00263 892019 529 0 0 201000 529 0.00263 998585 529 0 0 201000 529 0.00255 1.40886e+06 513 0 0 201000 513 0.00266 1.87236e+06 534 0 0 201000 534 0.00265 3.03691e+06 533 0 0 201000 533 0.00256 1.10325e+07 514 0 0 201000 514 #runout 0.00238 1.11591e+07 477 0 0 201000 477 #runout 0.00256 1.22183e+07 515 0 0 201000 515 #runout 0.00243 1.23561e+07 489 0 0 201000 489 #runout 0.00243 1.36844e+07 488 0 0 201000 488 #runout 0.00256 1.39004e+07 514 0 0 201000 514 #runout 0.00256 1.53945e+07 514 0 0 201000 514 #runout #Rotating bending data below. #Unaged specimens, Longitudinal 0.00272 238242 547 0 0 201000 547 0.00264 254227 530 0 0 201000 530 0.00274 726451 550 0 0 201000 550 0.00253 771359 509 0 0 201000 509 0.00249 1.21286e+06 501 0 0 201000 501 0.00255 2.60549e+06 512 0 0 201000 512 0.00255 6.72323e+06 513 0 0 201000 513 0.00243 1.13417e+07 488 0 0 201000 488 #runout 0.00236 3.4222e+07 475 0 0 201000 475 #runout 0.00255 3.43838e+07 513 0 0 201000 513 #runout 0.00243 3.45847e+07 488 0 0 201000 488 #runout 0.00256 3.80882e+07 514 0 0 201000 514 #runout 0.00243 3.83114e+07 488 0 0 201000 488 #runout 0.00236 3.83202e+07 475 0 0 201000 475 #runout 0.00243 4.22113e+07 489 0 0 201000 489 #runout # #