# # AISI 9310steel. 4pt. Bending tests. AISI iter.184 HRc= 60 # Carburized specimen, Deep Case+Core. # Original bar: ElecFurnace,LadleRef.,Con-Cast, 40mm HotRolled bar # Original Chem.: 0.12C wt% .62Mn .007P .014S .19Si 3.12Ni 1.11Cr # .09Mo .16Cu .008Sn .022Al .003V .0002B .0012Ca .0066N .004As # Stress converted from loads using Mc/I analysis # Moment arm of load couple is 2 inch. I =0.00065104 in^4 # Tested by Wanhua Liang, UWaterloo 2017 #FileType= strain_life #DataType= raw #Name= SAE9310steel #Name= BendingSample #Name= AISI_Iter184 #Stress_Units= ksi #Strain_Units= strain #Sy= 0 #Su= 0 #E= 28687. #monotonic_K= 0 #monotonic_n= 0. #MaterialForm= bar #FailureDef= 50% load drop #BHN= 653 #Note!: Stress below are Bending Stress= Mc/I #where M is the bending moment. #StrAmp 2Nf StsAm So PlsStr iniEmod 0.00890 1108 240 0 0 26993 0.00836 4494 206 0 0 24632 0.00800 1426 217 0 0 27120 0.00722 6234 196 0 0 27191 0.00695 12068 158 0 0 22757 0.00680 9910 218 0 0 32082 0.00629 28790 183 0 0 29174 0.00593 37218 174 0 0 29423 #fisheye 0.00576 67670 167 0 0 28958 0.00565 105298 147 0 0 26039 #fisheye 0.00544 81498 168 0 0 30867 0.00541 27414 158 0 0 29217 0.00526 1465486 171 0 0 32487 #fisheye 0.00506 974476 135 0 0 26704 0.00482 139768 132 0 0 27514 0.00470 162864 167 0 0 35540 0.00495 2000000 134 0 0 27033 #runout 0.00470 2000000 140 0 0 29770 #runout 0.00413 2000000 130 0 0 31549 #runout # #