# # AISI 9310steel. 4pt. Bending tests. AISI iter.177 HRc= 37.4 # Simulated Carburized Core specimens. # Original Chem.: 0.12C wt% .62Mn .007P .014S .19Si 3.12Ni 1.11Cr # .09Mo .16Cu .008Sn .022Al .003V .0002B .0012Ca .0066N .004As # Stress converted from loads using Mc/I analysis # Moment arm of load couple is 2 inch. I =0.00065104 in^4 # Tested by Wanhua Liang, UWaterloo 2018 #FileType= strain_life #DataType= raw #Name= SAE9310steel #Name= BendingSample #Name= AISI_Iter177 #Stress_Units= ksi #Strain_Units= strain #Sy= 0 #Su= 0 #E= 29296. #monotonic_K= 0 #monotonic_n= 0. #MaterialForm= bar #FailureDef= 50% load drop #BHN= 348 HRc= 37.4 #StrAmp 2Nf StsAm So PlsStr iniEmod 0.009525 2694 194 0 0 30782 0.009510 2780 199 0 0 31807 0.008575 5114 187 0 0 27916 0.007195 10852 171 0 0 28803 0.007115 10418 176 0 0 32662 0.005750 18186 166 0 0 30402 0.005410 27570 158 0 0 29720 0.005390 55440 142 0 0 25869 0.005175 44356 142 0 0 30008 0.004409 240612 114 0 0 24292 0.004360 167148 117 0 0 29592 0.004165 241886 118 0 0 28525 0.003965 111714 128 0 0 31683 0.003942 184420 125 0 0 26382 0.003475 2000000 110 0 0 31683 0.003125 2000000 102 0 0 27076 #runout 0.003005 2000000 100 0 0 30402 #runout 0.002800 2000000 90 0 0 29720 #runout # #