# SAE9310 ThruCarburized Simul. Case, HRc=59 # AISI bar group Iter 168, Axial Specimens, Const. Ampl., # Gerdau Ht 1M66046 ElecFurn VacDegas LadleRefined # RotaryCast, HotRoll to 40mm bar # Original Chem: 0.12C .62Mn .007P .014S .19Si .16Cu 3.12Ni # 1.11Cr .09Mo .003V .022Al .0002B .008Sn 66ppm_N # Surface Carbon after H.T.= 0.60wt%, 0.2inch deep = 0.30wt%C # Retained Austenite= 23.4% See Cryderman Report of 2017 # Further Mean stress load control tests in D.Gaia thesis. # Tested by D.Gaia UWaterloo 2015 #FileType= strain_life #DataType= raw #Name= SAE9310 #Name= aisiIter168 #Name= ThruCarburized #Stress_units= MPa #Strain_units= strain #Sy= 764. #Su= 1019. #eu= 0.0094 #E= 199000 #%RA= 37. #monotonic_K= 4312. #monotonic_n= 0.273 #TrueFractureStress= 1019 #TrueFractureStrain= 0.0094 #MaterialForm= bar #FailureDef= 50% load drop #BHN= 634, Rockwell C= 59 #TotStrAmpl 2Nf StsAmpl So PlasStrAmpl InitialEmod 0.007850 226 1397 0.0 0.000830 199000 0.008009 1200 1494 0.0 0.000590 199000 0.005900 2028 1117 0.0 0.000290 199000 0.005210 3540 994 0.0 0.000210 199000 0.006520 3572 1195 0.0 0.000520 199000 0.005980 4132 1134 0.0 0.000280 199000 0.004740 8734 915 0.0 0.000150 199000 0.005310 10500 1014 0.0 0.000220 199000 0.005360 12774 982 0.0 0.000430 199000 0.003390 18058 655 0.0 0.000100 199000 0.003430 21570 672 0.0 0.000060 199000 0.003400 36234 684 0.0 0.000000 199000 0.002840 42652 547 0.0 0.000090 199000 0.002550 62396 499 0.0 0.000050 199000 0.002840 63240 558 0.0 0.000040 199000 0.003970 114482 752 0.0 0.000190 199000 0.002300 275408 478 0.0 0.000000 199000 0.002100 443380 446 0.0 0.000000 199000 0.002100 10369256 450 0.0 0.000000 199000 #Runout 0.002000 10000000 400 0.0 0.000000 199000 #Runout 0.002000 10000000 423 0.0 0.000000 199000 #Runout 0.002000 10000000 411 0.0 0.000000 199000 #Runout # #