# SAE9310 Q+T Simul. Carburized Core, AISI Iter 127 HRc=37.9 # Constant Ampl., Axial. # Gerdau Ht.4M64977 ElecFurn. VacDegas LadleRefined RotaryCast # Hot Rolled Control Cooled 15.2mm bar, Simulated Carburized Core. # Chem.: 0.13wt%C .47Mn .008P .005S .22Si .18Cu 3.08Ni # 1.10Cr .09Mo .004V .003Nb .018Al .12Sn 102ppm_N # Inclusion Rating TypeA=1.0T 0.5H TypeB=0.5T 0.0H TypeC=0 TypeD=1.0T 0.0H # Tested UoWaterloo 2011 #FileType= strain_life #DataType= raw #Name= SAE9310 #Name= AISIit.127 #Units= MPa #Sy= 990.0 #Su= 1201.0 #E= 194500 #eu= 0.040 engr. strain at Su #monotonic_K= 1796.0 #monotonic_n= 0.094 #MaterialForm= bar #TrueFractureStress= 2172 #TrueFractureStrain= 0.832 #%RA= 56.5 % #%Elongation= 8.8 % over 0.3inch gauge #Hardness, Rockwell C= 37.9 #BHN= 352 #StrAmpl 2Nf StsAmpl So PlsStrAmpl Emod 0.021240 204 1061 0.0 0.015440 194500 #None 0.020950 230 1002 0.0 0.015470 194500 #None 0.021300 230 1024 0.0 0.015700 194500 #None 0.010500 1872 897 0.0 0.005780 194500 #None 0.010790 1994 926 0.0 0.005910 194500 #None 0.005010 14668 739 0.0 0.001180 194500 #None 0.005030 15000 756 0.0 0.001110 194500 #None 0.005050 27266 767 0.0 0.001080 194500 #None 0.002960 1829456 548 0.0 0.000120 194500 #None 0.002940 2144144 548 0.0 0.000110 194500 #None 0.002930 3513540 542 0.0 0.000130 194500 #None 0.002560 3774562 479 0.0 0.000080 194500 #None 0.002630 4726222 490 0.0 0.000100 194500 #None 0.002640 4882916 474 0.0 0.000190 194500 #None 0.002520 7408730 456 0.0 0.000160 194500 #None 0.002510 7969424 467 0.0 0.000100 194500 #None 0.002740 10000000 485 0.0 0.000240 194500 #Runout 0.002540 10000000 459 0.0 0.000240 194500 #Runout #Carbon, %= 0.13 #Manganese, %= 0.47 #Phosphorus, %= 0.008 #Sulfur, %= 0.005 #Silicon, %= 0.22 #Copper, %= 0.18 #Nickel, %= 3.08 #Chromium, %= 1.10 #Molybdenum, %= 0.09 #Vanadium, %= 0.004 #Columbium/Niobium, %= 0.003 #Aluminum, %= 0.018 #Tin, %= 0.012 #Nitrogen, ppm= 102 # #