# SAE9310 Q+T Simul. Carburized Core, AISI Iter 125 HRc=35.2 # Constant Ampl., Axial. # Gerdau Ht.4M64977 ElecFurn. VacDegas LadleRefined RotaryCast # Hot Rolled Control Cooled 25.4mm bar Simulated Carburized Core. # Chem.: 0.13wt%C .47Mn .008P .005S .22Si .18Cu 3.08Ni # 1.10Cr .09Mo .004V .003Nb .018Al .12Sn 102ppm_N # Inclusion Rating TypeA=1.0T 0.5H TypeB=0.5T 0.0H TypeC=0 TypeD=1.0T 0.0H # Tested UoWaterloo 2011 #FileType= strain_life #DataType= raw #Name= SAE9310 #Name= AISIit.126 #Units= MPa #Sy= 850.0 #Su= 1085.0 #E= 195800 #eu= 0.050 engr. strain at Su #monotonic_K= 1633.0 #monotonic_n= 0.105 #MaterialForm= bar #%RA= 57.5 % #%Elongation= 9.9 % #TrueFractureStress= 2155 #TrueFractureStrain= 0.857 #Hardness, Rockwell C= 35.2 #BHN= 331 #StrAmpl 2Nf StsAmpl So PlsStrAmpl Emod 0.020980 292 1019 0.0 0.015620 195800 #None 0.021080 306 933 0.0 0.016170 195800 #None 0.021080 308 923 0.0 0.016220 195800 #None 0.009040 1806 811 0.0 0.004820 195800 #None 0.008830 2320 865 0.0 0.004330 195800 #None 0.008990 2500 765 0.0 0.005010 195800 #None 0.005140 15122 667 0.0 0.001690 195800 #None 0.005040 22028 724 0.0 0.001290 195800 #None 0.005050 30946 721 0.0 0.001320 195800 #None 0.003050 280684 546 0.0 0.000220 195800 #None 0.003040 659848 555 0.0 0.000170 195800 #None 0.002770 1644688 526 0.0 0.000050 195800 #None 0.003020 1785358 569 0.0 0.000080 195800 #None 0.002810 2532076 517 0.0 0.000130 195800 #None 0.002530 6445226 478 0.0 0.000050 195800 #None 0.002770 6582088 506 0.0 0.000160 195800 #None 0.002500 10000000 461 0.0 0.000110 195800 #Runout 0.002520 10000000 478 0.0 0.000050 195800 #Runout #Carbon, %= 0.13 #Manganese, %= 0.47 #Phosphorus, %= 0.008 #Sulfur, %= 0.005 #Silicon, %= 0.22 #Copper, %= 0.18 #Nickel, %= 3.08 #Chromium, %= 1.10 #Molybdenum, %= 0.09 #Vanadium, %= 0.004 #Columbium/Niobium, %= 0.003 #Aluminum, %= 0.018 #Tin, %= 0.012 #Nitrogen, ppm= 102 # #