# Note: Periodic Overload Tests !
# AISI 8615+Carburized Bending samples  AISI Iter 163 "Deep Case"
# Carburized Case/Core Composite 4 pt Bend. specimen. Constant Ampl
# CrossSection= 0.25inch deep  x 0.50in wide,  Kt= 1.0
# See Chrysler Metallurgy and Hardness report #144326
# Chem. Before Carburized wt%: 0.11C .84Mn .009P .035S
# .30Si .15Cu .40Ni .60Cr .20Mo .005V .002Nb .03Al
# ElecFurnace=True VacuumDegas=True LadleRefined=True ConCast= True
# Austen. at 1700F w 0.9%C potential for 3.5hrs, Step down to 1500F then
# Quench in 150F oil, temper at 400F.
# HRc Hardness profile: Surface=60, 50@.028", 35@.05"
# Core has lots of ferrite.
# Tested by A.El-Menoufy, U.Waterloo.

#FileType= strain_life
#DataType = raw
#Name= SAE8615bend
#Name= Carburized
#Name= Iter-164
#Units= MPa
#E= 206824  ??  Probably not from bending specimen.?
#RawMaterialForm= bar
#FailureDef= 50% load drop

#Note!! : Loads were not recorded in these tests.

#TotStrAmpl 2Nf StsAmpl MeanSts, CalcPlasStrAmpl InitialElas Mod
0.005500 380 0 0.0 0.000000 0
0.005500 3200 0 0.0 0.000000 0
#0.004500 13890 0 0.0 0.000000 0
#0.004500 17690 0 0.0 0.000000 0
#0.004400 33920 0 0.0 0.000000 0
#Tests above are Const. Ampl from iter 163
#A "#" as 1st char comments out the line

#Tests below are Periodic Overload (Loads not observed)
0.0016  28231  0  0  0  0
0.0013  36126  0  0  0  0
0.001   27195  0  0  0  0
0.0007  240628  0  0  0  0
0.0002  1620291  0  0  0  0
0.0002  1326841  0  0  0  0
0.0002  2439530  0  0  0  0
0.0002  2951908  0  0  0  0
0.0002  1455621  0  0  0  0
0.0003  1089933  0  0  0  0