# Note ! Periodic Overload tests ! # AISI 8822 Quenched+temp. Simul. Core HRc=40 High Side Chemistry # Original Bar: ElecFurn. VacDegas LadleRef Concast HotRolled 34mm # Martensite, %= 100 # Chem.(before Carb.): wt% .22C .86Mn .013P .025S .17Si .24Cu # 0.43Ni 0.54Cr .39Mo .004V .028Al # Tested by U.Waterloo #FileType= strain_life #DataType= raw #Name= SAE8822 #Name= Simul.Carb.Core #Name= Iter110 #Stress_units= MPa #Strain_units= strain #Sy= 1528.0 #Su= 1723.0 #E= 208000 #monotonic_K= 2175.0 #monotonic_n= 0.057 #Reduc.Area, Fract.Strain, and Fract.Stress appear incorrect in report. #MaterialForm= bar #FailureDef= 50% load drop #BHN= 375 from HRc= 40 #StrAmpl 2Nf StsAmpl So PlsStrAmp Init.Modulus 0.010240 600 1226 0.0 0.004350 208000. #None 0.010250 824 1156 0.0 0.004690 208000. #None 0.010050 962 1187 0.0 0.004340 208000. #None 0.006980 2972 1074 0.0 0.001810 208000. #None 0.007050 3018 1093 0.0 0.001790 208000. #None 0.007040 3746 1070 0.0 0.001890 208000. #None 0.005970 4160 1008 0.0 0.001130 208000. #None 0.006460 5144 1087 0.0 0.001230 208000. #None 0.004980 9256 940 0.0 0.000450 208000. #None 0.003970 25128 847 0.0 0.000000 208000. #None 0.004000 54560 755 0.0 0.000370 208000. #None 0.004440 58888 739 0.0 0.000890 208000. #None 0.004040 71188 743 0.0 0.000470 208000. #None 0.003590 98484 776 0.0 0.000000 208000. #None 0.003500 274260 728 0.0 0.000000 208000. #None 0.002970 10000000 626 0.0 0.000000 208000. #Runout 0.002970 10000000 626 0.0 0.000000 208000. #Runout 0.002970 10000000 626 0.0 0.000000 208000. #Runout # #