#
# # Fitted Curve ! # SAE8620 Thru Carburized Rc=59 # BasicOxygen, LadleRefined, ConCast(381x508mm), HotRolled to 82.6mm bar # Specimens machined, thru carburized, polished. # Inclusions: TypeD= 1 Thin, TypeA,B,C=none # Test: UoWaterloo, M.Khalil, T.Topper Jan.2001 # saedigcurve_v2.2.f starts. #FileType= strain_life #DataType= fitted #Name= SAE8620 #Name= AisiIt_38 #Name= ThruCarburized #Stress_units= MPa #Strain_units= strain #Sy= 920.0 #Su= 1202.0 #E= 202000 #monotonic_K= 2335.0 #monotonic_n= 0.122 #FractureStrain= 0.011 #FractureStress= 1150. #%RA= 1. #MaterialForm= bar #FailureDef= 50% load drop #BHN= 583 #Hardness, Rockwell C= 59 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus #Basic Oxygen= True #Electric Furnace= False #Vacuum Degas= False #Ladle Refined= True #Ingot Cast= False #Continuous Cast= True #Martensite, %= 100 #Carbon, %= 0.23 (prior to carburize) #Manganese, %= 0.82 #Phosphorus, %= 0.011 #Sulfur, %= 0.027 #Silicon, %= 0.25 #Copper, %= 0.02 #Nickel, %= 0.48 #Chromium, %= 0.5 #Molybdenum, %= 0.18 #Vanadium, %= 0.01 #Columbium/Niobium, %= 0.00 #Lead, %= 0.001 #Titanium, %= 0.003 #Tin, %= 0.003 #Nitrogen, ppm= 40 # SAE8620 AisiIt_38 BHN= 583 Fn= 0 # Monotonic Props. Cyclic Props. #ELAS. MOD.= 29298. KSI, 202. GPA K' =6105.3 KSI, 42095.MPA #YIELD,0.2%= 133. KSI, 920. MPA N' = 0.5461 #ULT. STRG.= 174. KSI, 1202. MPA F. STRG COEF= 170.0 KSI, 1172.MPA #K = 0.0 KSI, 0. MPA F.STRG EXP, b=-0.0603 #N = 0.0000 FAT DUCT COEF= 0.0014 #RED. IN AREA = 1.0 F.DUCT EXP, c=-0.1104 #T. FRAC. STG.= 166.8 KSI, 1150. MPA Exp Cyc Yld = 205. Ksi,1414.MPA #T. FRAC. STR.= 0.011 Fit Cyc Yld = 150. Ksi,1032.MPA #No. fatigue data points= 19 # # NOTE!! The Following Points are FITTED DATA:#NOTE!! Fitted Stress computed using Experm. K' and n' #Stress_Units= MPa # Total Strain 2Nf Stress Mean Plastic Strain Initial # Amp Amp Stress Amp Elastic Mod. 0.00722 1 1039.6 0. 0.00207 202000. #Fitted_point 0.00688 2 1016.2 0. 0.00185 202000. #Fitted_point 0.00645 5 984.9 0. 0.00158 202000. #Fitted_point 0.00615 10 960.9 0. 0.00139 202000. #Fitted_point 0.00586 20 936.8 0. 0.00122 202000. #Fitted_point 0.00550 50 904.6 0. 0.00103 202000. #Fitted_point 0.00525 100 879.9 0. 0.00089 202000. #Fitted_point 0.00501 200 855.2 0. 0.00077 202000. #Fitted_point 0.00470 500 822.2 0. 0.00063 202000. #Fitted_point 0.00449 1000 797.1 0. 0.00054 202000. #Fitted_point 0.00428 2000 772.0 0. 0.00046 202000. #Fitted_point 0.00403 5000 738.7 0. 0.00037 202000. #Fitted_point 0.00384 10000 713.7 0. 0.00031 202000. #Fitted_point 0.00367 20000 688.8 0. 0.00026 202000. #Fitted_point 0.00345 50000 656.2 0. 0.00020 202000. #Fitted_point 0.00330 100000 632.0 0. 0.00017 202000. #Fitted_point 0.00315 200000 608.1 0. 0.00014 202000. #Fitted_point 0.00296 500000 577.2 0. 0.00011 202000. #Fitted_point 0.00283 1000000 554.4 0. 0.00009 202000. #Fitted_point 0.00270 2000000 532.2 0. 0.00007 202000. #Fitted_point 0.00255 5000000 503.8 0. 0.00005 202000. #Fitted_point 0.00243 10000000 483.1 0. 0.00004 202000. #Fitted_point 0.00233 20000000 463.0 0. 0.00003 202000. #Fitted_point 0.00219 50000000 437.6 0. 0.00003 202000. #Fitted_point 0.00210 100000000 419.2 0. 0.00002 202000. #Fitted_point 0.00200 200000000 401.4 0. 0.00002 202000. #Fitted_point 0.00189 500000000 379.1 0. 0.00001 202000. #Fitted_point 0.00181 1000000000 362.9 0. 0.00001 202000. #Fitted_point # #