# # SAE51B60 Q+T .0021% Boron, AISI Iter. 33, HRc=45 # Material cyclically softens from Sy=1830 to Cyclic_Sy=1280. # NorthStar: ElecFurnace, ConCast(152x152mm), HotRolled to 82.3mm # Spec machined, then heat treated (Q in oil), tempered, polished. # Chem.: 0.58wt%C .86Mn .008P .013S .26Si .01Cu .07Ni .81Cr # .04Mo .01V 0Nb .027Al 0Pb .041Ti .01Cobalt .0021B # Inclusions: TypeA,B,C none, TypeD= 1 # Typical part= springs, 100% Martensite # Test: UoWaterloo M.Khalil, T.Topper Revised Feb.2000 #FileType= strain_life #DataType= raw #Name= SAE51B60 #Name= Quench+Temper #Name= AisiIt_33 #Stress_units= MPa #Strain_units= strain #Sy= 1830.0 #Su= 1970.0 #eu= 0.044 engr. strain at Su #E= 200000 #monotonic_K= 2332.0 #monotonic_n= 0.039 #FractureStrain= 0.20 #FractureStress= 1968. #%RA= 21.6 #%Elongation= 36 % over 0.3inch gauge #MaterialForm= bar #FailureDef= 50% load drop #BHN= 450 #Hardness, Rockwell C= 45 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0100 1998 1349 0.0 0.00322 190000 #None 0.0100 2416 1349 0.0 0.00322 201000 #None 0.0100 2870 1327 0.0 0.00334 190000 #None 0.0080 4324 1256 0.0 0.00171 200000 #None 0.0080 5602 1256 0.0 0.00172 200000 #None 0.0080 7060 1249 0.0 0.00178 193000 #None 0.0060 15802 1203 0.0 0.00000 204000 #None 0.0060 17014 1208 0.0 0.00000 202000 #None 0.0050 84880 1015 0.0 0.00000 203000 #None 0.0050 120000 1072 0.0 0.00000 200000 #None 0.0042 366782 876 0.0 0.00000 200000 #None 0.0045 397400 939 0.0 0.00000 207000 #None 0.0042 446926 876 0.0 0.00000 200000 #None 0.00443 793076 918 0.0 0.00000 207000 #None 0.00399 882912 833 0.0 0.00000 198000 #None 0.00400 1472236 834 0.0 0.00000 200000 #None 0.00379 1532132 792 0.0 0.00000 195000 #None 0.00369 10000000 771 0.0 0.00000 200000 #Runout 0.00399 10000000 833 0.0 0.00000 204000 #Runout 0.00400 10000000 834 0.0 0.00000 206000 #Runout #Carbon, %= 0.59 #Manganese, %= 0.86 #Phosphorus, %= 0.008 #Sulfur, %= 0.013 #Silicon, %= 0.26 #Copper, %= 0.10 #Nickel, %= 0.07 #Chromium, %= 0.81 #Molybdenum, %= 0.04 #Vanadium, %= 0.01 #Columbium/Niobium, %= 0.00 #Aluminum, %= 0.027 #Lead, %= 0.000 #Titanium, %= 0.041 #Cobalt, %= 0.010 #Boron, %= 0.0021 # #