# SAE4320 Simul. Carburized Core, AISI Iter.147 HRc= 30.4 # Note!: Periodic Overload tests # Gerdau Ht.M28431 ElecFurn. VacDegas ConCast HotRoll 22.9mm bar # 60%Bainite, 30%Martensite, 10%Ferrite # Original Chem.: 0.19wt%C .62Mn .007P .025S .24Si .16Cu 1.76Ni # 0.50Cr .25Mo .004V .002Nb .028Al .0005Pb .002Ti .01Cobalt .0001B # 0Zr .007Sn 15ppm_O 61ppm_N # Inclusion Rating: TypeA=1.0T 0.5H TypeB=1.0T 0.0H TypeC=0 TypeD=1.0T 0.5H # Short life tests from CA Iter.123, Long life are POL tests. # Tested by UoWaterloo 2011 #FileType= strain_life #DataType= raw #Name= SAE4320 #Name= AISIit.147 #Name= SimulCore #Units= MPa #Sy= 745 #Su= 1010 #eu= 0.032 engr. strain at Su #E= 194300 #monotonic_K= 1219 #monotonic_n= 0.058 #MaterialForm= bar #%Elongation= 11.3 % ? seems too low. #%RA= 57 % #TrueFractureStress= 1984 #TrueFractureStrain= .846 #FailureDef= 50% load drop #Hardness, Rockwell C= 30.4 #BHN= 289 #StrAmpl 2Nf StsAmpl So PlsStrAmpl Emod #0.010080 1106 763 0.0 0.006020 194300 #None #0.008630 1878 676 0.0 0.005040 194300 #None #0.008080 3764 706 0.0 0.004340 194300 #None #0.006420 5508 705 0.0 0.002700 194300 #None #0.007030 5700 686 0.0 0.003400 194300 #None #0.006170 10880 641 0.0 0.002780 194300 #None #0.005400 12500 630 0.0 0.002090 194300 #None #0.004750 24948 604 0.0 0.001580 194300 #None #0.004270 42760 605 0.0 0.001090 194300 #None #0.003710 89462 570 0.0 0.000730 194300 #None #0.003080 201438 529 0.0 0.000310 194300 #None #0.002850 377226 517 0.0 0.000140 194300 #None #0.002800 818692 505 0.0 0.000150 194300 #None #0.002780 985868 497 0.0 0.000190 194300 #None #0.002730 1124582 492 0.0 0.000160 194300 #None #0.002740 3608952 523 0.0 0.000000 194300 #None #0.002730 9639036 492 0.0 0.000160 194300 #None #0.002570 20000000 466 0.0 0.000130 194300 #Runout #0.002690 20000000 473 0.0 0.000210 194300 #Runout #Tests above are Const. Ampl. from Iter.123 #Comment lines begin with "#" #Below are Periodic Overload tests. #Mean stress and plastic strains were not reported. 0.00162 3135406 312 0 0 194300 0.00118 14801794 227 0 0 194300 0.00125 14166910 241 0 0 194300 0.00177 2475380 340 0 0 194300 0.00140 5719056 269 0 0 194300 0.00155 9063722 297 0 0 194300 0.00133 5752198 255 0 0 194300 0.00184 1728936 354 0 0 194300 0.00199 1413692 382 0 0 194300 0.00214 1117428 411 0 0 194300 0.00155 9216964 297 0 0 194300 #Carbon %= 0.19 #Manganese %= 0.62 #Phosphorus %= 0.0070 #Sulfur %= 0.025 #Silicon %= 0.24 #Copper %= 0.16 #Nickel %= 1.76 #Chromium %= 0.50 #Molybdenum %= 0.25 #Vanadium %= 0.004 #Columbium/Niobium %= 0.0020 #Aluminum %= 0.0280 #Lead %= 0.0005 #Titanium %= 0.0020 #Calcium %= 0.0006 #Cobalt %= 0.008 #Zirconium %= 0.0020 #Boron %= 0.0001 #Tin %= 0.0070 #Oxygen ppm= 15. #Nitrogen ppm= 61. # #