# # SAE1541 ColdSized BHN= 195 AISI Iter.002 # RepublicSteel HT 8997982, BasicOx LadleRef ConCast # Bloom Size 310x372mm ColdSized to 19mm bar # Pearlite=66% Ferrite=32% Inclusions: TypeA,B,C=0 TypeD= 2.5 # Tested by UWaterloo #FileType= strain_life #DataType= raw #Name= SAE1541 #Name= AisiIt_002 #Stress_units= MPa #Strain_units= strain #Sy= 461.0 #Su= 905.5 #eu= 0.046 strain at Su #E= 196000 #monotonic_K= 1543.5 #monotonic_n= 0.163 #LowerYield= 461 #UpperYield= 472 #MaterialForm= bar #FailureDef= 50% load drop #BHN= 195 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0100 1634 585 0.0 0.00702 208000 #None 0.0100 1696 581 0.0 0.00704 183000 #None 0.0100 1856 684 0.0 0.00652 205000 #None 0.0100 2520 498 0.0 0.00746 191000 #None 0.0070 4002 524 0.0 0.00434 194000 #None 0.0070 4552 502 0.0 0.00445 188000 #None 0.0070 5256 512 0.0 0.00440 199000 #None 0.0070 6510 508 0.0 0.00442 191000 #None 0.0057 9666 464 0.0 0.00334 191000 #None 0.0057 10000 500 0.0 0.00316 206000 #None 0.0057 11676 476 0.0 0.00328 199000 #None 0.0057 12510 494 0.0 0.00319 202000 #None 0.0032 40000 451 0.0 0.00090 198000 #None 0.0032 53984 408 0.0 0.00113 193000 #None 0.0032 61490 416 0.0 0.00109 198000 #None 0.0032 74142 420 0.0 0.00106 202000 #None 0.0028 88018 412 0.0 0.00070 195000 #None 0.0028 88470 408 0.0 0.00073 198000 #None 0.0028 96166 406 0.0 0.00074 198000 #None 0.0028 111208 423 0.0 0.00064 197000 #None 0.0022 554910 390 0.0 0.00022 195000 #None 0.0022 1636400 378 0.0 0.00028 195000 #None 0.0022 4999800 388 0.0 0.00023 195000 #None 0.0020 10000000 380 0.0 0.000070 193000 #Runout Adjusted plas strain value #Carbon, %= 0.42 #Manganese, %= 1.4 #Phosphorus, %= 0.011 #Sulfur, %= 0.1 #Silicon, %= 0.18 #Copper, %= 0.10 #Nickel, %= 0.05 #Chromium, %= 0.07 #Molybdenum, %= 0.01 #Vanadium, %= 0.00 #Columbium/Niobium, %= 0.00 #Aluminum, %= 0.001 #Titanium, %= 0.001 #Calcium, %= 0.00 #Boron, %= 0.0024 #Oxygen, ppm= 20 #Here is the bottom part of the html graph/calc wrapper----------- # #