# # SAE1117 Thru Carburized Simul. Case AISI_iter052 HRc=62 # MacSteel ElectFurn. ConCast RotaryCast HotRolled 44.5mm bar # 100%Martensite, TypeD Globular Inclusions Rate=1 # Original Chem: .18C 1.22Mn .012P .215S .14Si .11Cu .03Ni .12Cr # .02Mo 0V 0Columb .01Sn 63ppmN # Tested at M.Khalil UWaterloo 2002 #FileType= strain_life #DataType= raw #Name= SAE1117 #Name= AisiIt_52 #Name= ThruCarbSimulCase #Stress_units= MPa #Strain_units= strain #Sy= 0 # it never yielded. #Su= 880.0 #eu= 0.0048 strain at Su #E= 184000 #monotonic_K= 23179.0 #monotonic_n= 0.441 #RA= 0. 0.49 reported? probably zero #TrueFractureStress= 745 mpa #TrueFractureStrain= 0.0048 #%Elongation= 0.48 % elastic failure #MaterialForm= bar #FailureDef= 50% load drop #BHN= 625 #Hardness, Rockwell C= 62 #StrAmp 2Nf StsAmp So PlasStr InitialModulus 0.0050 1 897 0.0 0.00012 180000 #None 0.0045 1 811 0.0 0.00010 180000 #None 0.0050 1 897 0.0 0.00013 179000 #None 0.0040 3312 761 0.0 0.00000 188000 #None 0.0040 3570 758 0.0 0.00000 190000 #None 0.0045 8732 813 0.0 0.00011 180000 #None 0.0020 9988 366 0.0 0.00000 184000 #None 0.0045 10700 811 0.0 0.00009 181000 #None 0.0035 18020 639 0.0 0.00000 183000 #None 0.0032 21718 573 0.0 0.00000 180000 #None 0.0030 32274 548 0.0 0.00000 183000 #None 0.0035 37112 639 0.0 0.00000 182000 #None 0.0026 171220 454 0.0 0.00000 176000 #None 0.0026 434224 462 0.0 0.00000 182000 #None 0.0018 605182 333 0.0 0.00000 185000 #None 0.0021 787038 371 0.0 0.00000 185000 #None 0.0019 1216000 338 0.0 0.00000 181000 #None 0.0018 1755592 327 0.0 0.00000 183000 #None 0.0018 10000000 316 0.0 0.00000 184000 #Runout 0.0018 10000000 330 0.0 0.00000 183000 #Runout # #