# # SAE1117 Quench+Temp. Simul. Carb. Core HRB=94 AISI It.051 HRc=(14) # MacSteel ElectFurn. ConCast RotaryCast HotRolled 44.5mm bar # 100% Martensite, TypeD Globular Inclusions Rate=2 # Original Chem: .18C 1.22Mn .012P .215S .14Si .11Cu .03Ni .12Cr # .02Mo 0V 0Columb .01Sn 63ppmN # Tested at UWaterloo 2001 #FileType= strain_life #DataType= raw #Name= SAE1117 #Name= AisiIt_51 #Name= Q+Tsimul.Core #Stress_units= MPa #Strain_units= strain #Sy= 655.0 #Su= 777.0 #eu= 0.060 engr. Strain at Su #E= 202000 #monotonic_K= 973.0 #monotonic_n= 0.626 #MaterialForm= bar #FailureDef= 50% load drop #%Elongation= 37 #%RA= 55 #TrueFractureStress= 1238 #TrueFractureStrain= 0.80 #BHN= 193 #Hardness, Rockwell B= 94 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0102 1200 621 0.0 0.00710 203000 #None 0.0099 1362 638 0.0 0.00670 204000 #None 0.0101 2080 599 0.0 0.00713 203000 #None 0.0102 2400 599 0.0 0.00724 203000 #None 0.0081 4264 570 0.0 0.00531 201000 #None 0.0081 4570 592 0.0 0.00517 204000 #None 0.0083 5066 576 0.0 0.00546 202000 #None 0.0060 11520 530 0.0 0.00333 204000 #None 0.0061 11660 511 0.0 0.00353 201000 #None 0.0060 11780 547 0.0 0.00328 204000 #None 0.0040 36140 518 0.0 0.00148 203000 #None 0.0041 47782 438 0.0 0.00193 201000 #None 0.0021 137420 402 0.0 0.00011 191000 #None 0.0021 195908 402 0.0 0.00008 203000 #None 0.0019 401136 379 0.0 0.00000 202000 #None 0.0016 10000000 313 0.0 0.00000 201000 #Runout 0.0017 10000000 341 0.0 0.00000 201000 #Runout 0.0015 10000000 313 0.0 0.00000 203000 #Runout # #