# SAE 1151V HotFormed Controlled Cool, AISI Iter.027 HRc=22 # Chrysler/Slater Steel: Elec.Furn. Concast, HotForm Control Cool 25mm bar # Connecting Rod material. # Chem.: 0.48 .88Mn .009P .08S .20Si .12Cu .06Ni .07Cr .02Mo .03V # Pearlite, %= 75 Ferrite, %= 25 ASTM Grain Size No.= 4 to 5 # Tested by F.Yin UoToledo, 2001 #FileType= strain_life #DataType= raw #Name= SAE1151V #Name= AisiIt_27 #Name= HotFormControlCool #Stress_units= MPa #Strain_units= strain #Sy= 452.3 #Su= 760.8 #eu= 0.10 avg engr.strain at Su #E= 206000 #monotonic_K= 1345.9 #monotonic_n= 0.190 #LowerYield= 446.3 #UpperYield= 496.2 #MaterialForm= bar #FailureDef= 50% load drop #%RA= 50.6 % #%Elongation= 26.3 % over 0.3inch #BHN= 205 #Hardness, Rockwell B= 99 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0199 446 694 10.9 0.01656 212000 #IGL 0.0199 470 720 3.3 0.01643 212000 #IGL 0.0200 548 697 -10.7 0.01660 209000 #IGL 0.0100 2328 582 -0.6 0.00716 209000 #IGL 0.0100 2550 571 -4.5 0.00723 205000 #IGL 0.0100 2736 566 -5.0 0.00725 206000 #IGL 0.0060 8452 510 -3.1 0.00352 207000 #IGL 0.0060 9316 490 6.0 0.00362 206000 #IGL 0.0060 9556 494 -1.5 0.00359 210000 #IGL 0.0035 37574 404 -0.4 0.00151 216000 #IGL 0.0035 41076 415 -0.7 0.00146 208000 #IGL 0.0035 41314 424 1.8 0.00142 211000 #IGL 0.0020 281092 341 3.1 0.00034 203000 #IGL 0.0020 281858 336 19.9 0.00034 205000 #IGL 0.0020 305288 337 22.6 0.00035 208000 #IGL 0.0015 2957606 297 21.1 0.00007 209000 #IGL 0.0000 10000000 298 0.0 0.00000 0000 #Runout 0.0000 10000000 298 0.0 0.00000 0000 #Runout #Carbon, %= 0.48 #Manganese, %= 0.88 #Phosphorus, %= 0.009 #Sulfur, %= 0.08 #Silicon, %= 0.2 #Copper, %= 0.12 #Nickel, %= 0.06 #Chromium, %= 0.07 #Molybdenum, %= 0.02 #Vanadium, %= 0.03 #Here is the bottom part of the html graph/calc wrapper----------- # #