# SAE 1141V (0.05wt% V) Quench+Temper AisiIter. 16 HRc=22 # NorthStarStl.: ElecFurn. ConCast HotRolled 19mm bar # Reheat 1650F Oil Quench, 5%Bainite 90%Martensite 5%Ferrite # Chem.: 0.41%C 1.49Mn .017P .096S .18Si .09Cu .05Ni .11Cr .02Mo # .05V .01Sn # Inclusion Rating: Type A= 2 thin, Type B,C,D= 0 # Tested by M. Roessle UToledo 1998 #FileType= strain_life #DataType= raw #Name= SAE1141V #Name= Quench+Temper #Name= AisiIt_16 #Stress_units= MPa #Strain_units= strain #Sy= 609.7 #Su= 796.8 #eu= 0.092 engr. strain at Su #E= 215000 #monotonic_K= 1244.2 #monotonic_n= 0.141 #LowerYield= 601.2 #UpperYield= 626.9 #MaterialForm= bar #FailureDef= 50% load drop #%RA= 58 % #%Elongation= 34 % over 0.3inch gauge #BHN= 251.5 #Hardness, Rockwell C= 22 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0150 826 652 0.5 0.01195 207000 #IGL 0.0150 850 652 -0.1 0.01199 200000 #IGL 0.0150 906 659 0.1 0.01195 205000 #IGL 0.0100 2246 589 1.6 0.00726 206000 #IGL 0.0100 2338 589 0.9 0.00727 207000 #IGL 0.0100 2780 579 1.0 0.00732 207000 #IGL 0.0060 8052 537 3.1 0.00350 213000 #IGL 0.0060 8210 545 0.2 0.00347 202000 #IGL 0.0060 8350 527 3.0 0.00356 211000 #IGL 0.0035 46800 449 2.4 0.00141 211000 #IGL 0.0035 54220 449 12.3 0.00141 211000 #IGL 0.0035 57872 450 8.8 0.00141 205000 #IGL 0.0022 356750 390 75.9 0.00039 212000 #IGL 0.0022 399644 377 66.6 0.00045 207000 #IGL 0.0022 412500 393 99.5 0.00037 206000 #IGL 0.0018 10000000 343 0.0 0.00015 0000 #Runout 0.0017 10000000 343 134.5 0.00015 210000 #Runout 0.0018 10000000 343 0.0 0.00015 0000 #Runout #Carbon, %= 0.41 #Manganese, %= 1.49 #Phosphorus, %= 0.017 #Sulfur, %= 0.096 #Silicon, %= 0.18 #Copper, %= 0.09 #Nickel, %= 0.05 #Chromium, %= 0.1 #Molybdenum, %= 0.02 #Vanadium, %= 0.05 #Tin, %= 0.010 #Here is the bottom part of the html graph/calc wrapper----------- # #