# # SAE10V45 Normalized at 1650F AISIiter021 Rb=96, Bhn=212 HRc=(16) # Ispat Inland: BasicOxy,LadelRef ConCast(375x500), HotRolled to 82.5mmBar # Normalized at 1650F, Manuf.Specimens from bar. 9 spec. per # cross-section length. # Chem.: 0.48%C .82Mn .008P .028S .25Si .04Ni .18Cr .04Mo .027Al 150ppm_N # 60%Pearlite, 40%Ferrite, ASTM GrainSize(longit.)=8to9 # Inclusions: TypeA=1.5Thin, TypeB,C,D=0 # Tested by B.Li UoToledo #FileType= strain_life #DataType= raw #Name= SAE10V45 #Name= AisiIt_21 #Name= Normalized #Stress_units= MPa #Strain_units= strain #Sy= 465.2 #Su= 764.6 #E= 211000 (avg. of 19) reported=213000 #eu= 0.12 engr. strain at Su #monotonic_K= 1456.4 #monotonic_n= 0.223 #LowerYield= 464.4 #UpperYield= 499.7 #FractureStrain= 0.70 #FractureStress= 1131 #%RA= 48. #%Elongation= 26 % over 0.3 inch gauge #MaterialForm= bar #FailureDef= 50% load drop #BHN= 212 #Hardness, Rockwell B= 96 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0200 654 694 -2.9 0.01680 207000 #IGL 0.0200 656 691 -4.6 0.01683 217000 #IGL 0.0200 680 715 -33.6 0.01669 216000 #IGL 0.0100 3008 576 -0.7 0.00735 216000 #IGL 0.0100 3242 572 -2.1 0.00734 207000 #OGIT 0.0100 3380 574 -2.7 0.00736 211000 #IGL 0.0060 10400 486 -0.2 0.00376 207000 #IGL 0.0060 10824 492 -0.8 0.00374 203000 #IGL 0.0060 11840 492 -0.8 0.00374 208000 #IGL 0.0035 45976 399 2.2 0.00165 210000 #IGL 0.0035 52200 414 3.1 0.00160 220000 #IGL 0.0035 56200 408 0.3 0.00163 207000 #IGL 0.0023 215220 349 12.5 0.00065 210000 #IGL 0.0023 285380 351 9.6 0.00064 208000 #IGL 0.0023 313660 354 13.3 0.00063 209000 #IGL 0.0015 10000000 282 49.7 0.00021 215000 #Runout 0.0015 10000000 282 55.6 0.00019 213000 #Runout 0.0015 10000000 283 36.4 0.00019 212000 #Runout #Basic Oxygen= True #Electric Furnace= False #Vacuum Degas= False #Ladle Refined= True #Ingot Cast= False #Continuous Cast= True #Pearlite, %= 60 #Ferrite, %= 40 #ASTM Grain Size No. (Min to Max)= 8 to 9 #Carbon, %= 0.48 #Manganese, %= 0.82 #Phosphorus, %= 0.008 #Sulfur, %= 0.028 #Silicon, %= 0.25 #Nickel, %= 0.04 #Chromium, %= 0.18 #Molybdenum, %= 0.04 #Vanadium, %= 0.12 #Aluminum, %= 0.027 #Nitrogen, ppm= 150 # #