# # SAE 1090M (GM) Hot Form-Accelerated Cooled, Austempered AISI It.10 HRc=28 # RepublicSteel:BasicOxygen, LadleRef, HotRolled 50.8mm bar, # Hot Formed at 2100F, Austempered, Typical Stabilizer Bar material/process # 95% Pearlite, 5%Bainite # Type A inclusions of 1.5, Type B,C,D not seen. # Tensile has upper/lower yield type curve. # 0.88C .58Mn .002P .021S .22Si .28Cu .08Ni .14Cr .02Mo .03Va .002Ca # .0024B Al=lessThan .001 .001Ti 24ppm_O .003Nb # Test: U.Waterloo A.V-Farahani,T.Topper Sept May 1998 #FileType= strain_life #DataType= raw #Name= SAE1090forged #Name= Austempered #Name= AisiIt_10 #Stress_units= MPa #Strain_units= strain #Sy= 759.5 #Su= 1124.0 #eu= 0.073 engr. strain at Su #E= 214000 #monotonic_K= 1575.5 #monotonic_n= 0.108 #LowerYield= 759.5 #UpperYield= 772.7 #FractureStrain= 0.50 #FractureStress= 840 #%RA= 37.6 #%Elongation= 18 % over 0.3inch gauge #MaterialForm= bar #FailureDef= 50% load drop #BHN= 272 #Hardness, Rockwell C= 28 #StrAmp 2Nf StsAmp So CalcPlasStr InitialModulus 0.0100 2766 751 0.0 0.00650 219000 #None 0.0100 3046 793 0.0 0.00632 217000 #None 0.0100 3144 743 0.0 0.00654 217000 #None 0.0070 7000 710 0.0 0.00370 215000 #None 0.0070 7394 680 0.0 0.00384 215000 #None 0.0070 8630 674 0.0 0.00387 215000 #None 0.0057 11546 625 0.0 0.00279 220000 #None 0.0057 13350 615 0.0 0.00284 220000 #None 0.0057 13766 645 0.0 0.00270 220000 #None 0.0037 52700 549 0.0 0.00114 207000 #None 0.0037 55296 532 0.0 0.00122 207000 #None 0.0037 59796 551 0.0 0.00113 207000 #None 0.0032 77750 497 0.0 0.00088 220000 #None 0.0032 90000 495 0.0 0.00089 220000 #None 0.0031 97876 540 0.0 0.00068 220000 #None 0.0028 272774 505 0.0 0.00044 219000 #None 0.0026 1940920 464 0.0 0.00048 220000 #None 0.0026 10000000 441 0.0 0.00054 205000 #Runout 0.0026 10000000 434 0.0 0.00057 205000 #Runout 0.0026 10000000 462 0.0 0.00044 205000 #Runout #Carbon, %= 0.88 #Manganese, %= 0.58 #Phosphorus, %= 0.002 #Sulfur, %= 0.021 #Silicon, %= 0.22 #Copper, %= 0.28 #Nickel, %= 0.08 #Chromium, %= 0.14 #Molybdenum, %= 0.02 #Vanadium, %= 0.03 #Columbium/Niobium, %= 0.00 #Aluminum, %= 0.001 #Titanium, %= 0.001 #Calcium, %= 0.00 #Boron, %= 0.0024 #Oxygen, ppm= 24 # #