# # 16MnCr5(Modified) steel, 4pt Bend. Const.Ampl. # Four Pt bending tests of 16MnCr5 Steel HRc=38.2 # Simulated 1700F Carburized Core material. # Original Bar Chem.: # Stress converted from loads using Mc/I analysis # Moment arm of load couple is 2 inch. I =0.00065104 in^4 # There were mean loads observed during testing # Tested Wanhua Liang, UWaterloo, 2018 #FileType= strain_life #DataType= raw #Name= 16MnCr5steel #Name= CarburizedCore #Name= AISIiter205 #Stress_Units= ksi #Strain_Units= strain #Sy= 0 #Su= 0 #E= 28545. ! = Bending modulus= Stress/Strain #monotonic_K= 0 #monotonic_n= 0. #MaterialForm= bar #FailureDef= 50% load drop #BHN= 0 #!Note: Stress below calc. Elastic Stress= Mc/I #StrAmp 2Nf StsAm So PlsStr iniEmod 0.009060 4378 208 5 0 22967 0.008270 5608 193 0 0 23304 0.006995 9228 187 3 0 26762 0.004905 20292 161 0 0 32734 0.006480 21184 173 0 0 26741 0.004895 42896 142 0 0 28977 0.004445 55640 139 0 0 31208 0.004625 67392 129 0 0 27814 0.003785 129502 115 0 0 30436 0.003410 304050 99 0 0 28927 0.003110 359422 96 1 0 30791 0.003140 374300 87 0 0 27745 0.003080 394032 92 6 0 29844 0.003320 483160 97 4 0 29205 0.003009 659080 84 0 0 27916 0.003095 2000000 87 2 0 28149 #runout 0.002865 2000000 85 0 0 29654 #runout 0.002805 2000000 86 0 0 30631 #runout # #