# # AISI 16MnCr5 Modified Simulated Carbur. Core HRc=31.1 # Carburized at 1700F # Chem.: TBD # Tested by W.H.Liang U.Waterloo Apr 2018 # #FileType= strain_life #DataType= raw #TIMEcol= 0 #NAME= AISIiter204 #NAME= 16MnCr5Mod. #NAME= SimulCarbCore #Stress_units= mpa #Strain_units= strain #Sy= 1050. mpa #Su= 1370. mpa average of 2 tests #eu= 0.044 #strain at ultimate #E= 213822. mpa #TrueFractureStrain= 0.224 avg. of 2 #TrueFractureStress= 0 TBD #%RA= 0.4810 avg #BHN= 302. HRc=31.1 #Modulus below observed at low stress level on initial #loading in tension. #StrAmpl 2Nf StsAmpl So PlsStrAmp 1stLoadEmod NeubStsAmp 0.00966 2378 1035 -27 0.00467 207373 1440 0.00796 2494 1011 -23 0.00301 204269 1282 0.00860 3236 1026 -33 0.00376 212084 1368 0.00666 6640 949 -21 0.00196 201786 1129 0.00654 7368 963 -25 0.00198 210983 1153 0.00580 14640 901 3 0.00154 211545 1051 0.00490 27210 869 -43 0.00084 214010 955 0.00459 41204 846 -45 0.00059 211367 906 0.00500 46684 849 -85 0.00100 212014 949 0.00402 62170 801 -29 0.00025 212325 827 0.00415 81900 763 -60 0.00059 214440 824 0.00304 178740 678 82 0.00000 212640 662 0.00327 218940 657 -45 0.00017 211545 674 0.00331 258928 658 31 0.00030 218382 690 0.00284 531142 547 161 0.00027 212847 575 0.00276 10000000 561 0 0.00000 204739 563 #runout 0.00268 10000000 550 -8 0.00000 216434 565 #runout 0.00260 10000000 561 -6 0.00000 219031 565 #runout # #