# # AISI-16MnCr5 modified, Simulated 1900F Carb.Core HRc= 37.6 # Four Pt bending tests of AISI 16MnCr5(Mod) Core # OriginalMatl: ElecFurnace, VacDegas LadleRef Concast HotRollBar # Original Chem.: 0.16C wt% 1.22Mn .018P .034S .07Si .23Cu .11Ni 1.06Cr # .040Mo .002V .002Columb .02Al Source: Chrysler # Stress converted from loads using Mc/I analysis # Moment arm of load couple is 2.5 inch. I =0.00065104 in^4 # There were mean loads observed during testing #FileType= strain_life #DataType= raw #Name= AISI-16MnCr5mod-SimCore #Name= 4ptBendSample #Name= AISIiter197 #Stress_Units= mpa #Strain_Units= strain #Sy= 0 #Su= 0 #E= 177399 #monotonic_K= 0 #monotonic_n= 0. #MaterialForm= bar #FailureDef= 50% load drop #BHN= 349 from HRc= 37.56 #StrAmp 2Nf StsAm So PlsStr Emod 0.011067 1744 1427 0.00 0 128965 0.009300 3060 1293 0.00 0 139007 0.007600 4680 1187 0.00 0 156221 0.007067 6816 1196 0.00 0 169182 0.007067 10276 1111 0.00 0 157181 0.006000 12582 1034 0.00 0 172369 0.004967 30618 910 0.00 0 183243 0.004633 34512 863 0.00 0 186158 0.004500 42750 848 0.00 0 188457 0.003767 132512 662 0.00 0 175725 0.003267 149808 635 0.00 0 194390 0.002867 257280 565 0.00 0 196982 0.002600 759120 484 0.00 0 186158 0.002500 780720 449 0.00 0 179540 0.002367 503190 426 0.00 0 180041 0.002200 2000000 439 0.00 0 199321 #runout 0.002000 2000000 393 0.00 0 196501 #runout 0.002000 2000000 407 0.00 0 203740 #runout # #