# 16MnCr5steel Carburized to ShallowCase+core HRc=52.2 surface # 4Point Bending Specimen ! AISI Bar Group Iteration 190 # OriginalMatl: ElecFurnace, VacDegas LadleRef Concast HotRollBar # Original Chem.: 0.16C wt% 1.22Mn .018P .034S .07Si .23Cu .11Ni # 1.06Cr .040Mo .002V .002Columb .02Al # Note!: Bending Stress computed using Stress= Mc/I # U.Waterloo, Diogo DeSilva, 2016 #FileType= strain_life #DataType= raw #Name= 16MnCr5 #Name= AISI-Iter190 #Name= ShallowCase+Core #Stress_units= ksi #Strain_units= strain #Sy= 0. #Su= 0. #E= 30008 ksi !! bending stress/strain #TrueFractureStrain= 0 #TrueFractureStress= 0 #%RA= 0 #MaterialForm= bar #FailureDef= 50% load drop #BHN= 512 #HRc= 52.2 #Note: Stresses below are bending stress #StrAmpl 2Nf StsAmp So PlsStr Sts/Str # ksi ksi 0.00711 1406 209.0 0 0 29400 0.00711 2722 217.2 0 0 30547 0.00699 7050 210.2 0 0 30077 0.00605 57548 185.1 0 0 30590 0.00599 33818 157.5 0 0 26293 0.00599 19978 186.0 0 0 31057 0.0055 208080 170.4 0 0 30989 0.00544 26184 171.9 0 0 31595 0.00538 318368 171.4 0 0 31859 0.00514 220758 158.9 0 0 30922 0.00514 407974 157.2 0 0 30593 0.00503 658092 96.6 0 0 19208 0.00445 3843144 138.1 0 0 31031 0.00445 4000000 139.5 0 0 31354 #runout 0.00445 596534 138.8 0 0 31190 0.00427 4000000 134.7 0 0 31552 #runout 0.00427 4000000 130.9 0 0 30653 #runout 0.00422 4000000 131.8 0 0 31243 #runout # #