# 16MnCr5steel Carburized Quench+Temper to Simulate Core HRc=45 # AISI Bar Group Iteration 186 Axial Specimen tests. # OriginalMatl: ElecFurnace, VacDegas LadleRef Concast HotRollBar # Original Chem.: 0.16C wt% 1.22Mn .018P .034S .07Si .23Cu .11Ni # 1.06Cr .040Mo .002V .002Columb .02Al # Tested U.Mich Dearborn, 2017 #FileType= strain_life #DataType= raw #Name= 16MnCr5 #Name= AISI-Iter186 #Name= SimulatedCore #Stress_units= MPa #Strain_units= strain #Sy= 1040. #Su= 1398. #E= 201900 mpa average of initial Emods #monotonic_K= 1900. #monotonic_n= 0.082 #TrueFractureStrain= 0.38 compute from %RA #TrueFractureStress= 0 Not reported, assume 1400. #%RA= 32.0 #LowerYield= 1014 #UpperYield= 1067 #MaterialForm= bar #FailureDef= 50% load drop #BHN= 415 #HRc= 45 #StrAmpl 2Nf StsAmp So PlasStrAmp IniEmod 0.012 580 1119 0 0.00665 209000 0.012 684 1105 0 0.00664 206000 0.012 784 1103 0 0.00640 197000 0.01 978 1069 0 0.00484 207000 0.01 1300 1096 0 0.00468 206000 0.01 1440 1090 0 0.00180 133000 0.008 1806 1075 0 0.00219 185000 0.008 2450 998 0 0.00313 205000 0.008 2720 1074 0 0.00284 208000 0.008 3526 1033 0 0.00281 199000 0.006 5200 947 0 0.00164 217000 0.006 6800 927 0 0.00146 204000 0.006 9744 932 0 0.00145 205000 0.004 33000 777 0 0.00021 205000 0.004 33208 806 0 0.00013 208000 0.004 41654 794 0 0.00016 207000 0.0033 127856 695 0 0.00001 211000 0.002 2000000 399 0 0.00010 210000 #runout 0.0015 2000000 315 0 0.00003 214000 #runout # #