#Copyright (C) 2022 Fatigue Design + Evaluation Committee of the SAE. #This data file is free software; you can redistribute it and/or modify #it under the terms of the GNU General Public License as published by #the Free Software Foundation; either version 2 of the license, or (at #your option) any later version. #This data file is distributed in the hope that it will be useful, but #WITHOUT ANY WARRANTY; without even the implied warranty of MERCHANTA- #BILITY or FITNESS FOR A PARTICULAR PURPOSE. See the GNU General Public #License for more details. #You should have received a copy of the GNU General PUblic License along #with this program; if not, write to the Free Software Foundation, Inc., #59 Temple Place - Suite 330, Boston, MA 02111-1307, USA. Try also their #web site: http://www.gnu.org/copyleft/gpl.html # # AA5183 Aluminum Weld Metal # Spec. from a single pass of deposited weld metal from a # 1 inch aluminum butt weld. Hourglass shape with WM # limited to the gage section. Axis transverse to welding axis. # An extra spec. was machined with axis parallel to welding # axis for monotonic tension tests. # Ref.: J.D.Burk, F.V.Lawrence, jr., "The Effect of Residual Stresses # Ref.: on Weld Fatigue Life", U.of Illinois, Urbana, Jan. 1978 # Ref.: Dept. Metallurgical Engr., Fracture Control Report FCP No. 29 #FileType= strain_life #DataType= raw #TIMEcol= 0 #Name= AA5183 #Name= WeldMetal #Stress_Units= mpa #Strain_Units= strain #Sy= 138 mpa 20 ksi #Su= 299 43.3 #Emod= 71000 10300 #%RA= 33 % #FractureStress= 421 67 ksi #FractureStrain= 0.40 #n= 0.133 #K= 307 mpa 44.5 ksi #Cyclic_Sy= 269 mpa 39 ksi #StrAmpl 2Nf StsAmp So PlsStrAmpl Emod 0.0102 178 362 0 0.0052 71000 0.0073 468 336 0 0.0027 71000 0.0052 2078 316 0 0.0007 71000 0.0042 9956 281 0 0.0001 71000 0.0031 67004 217 0 0 71000 0.0027 146356 190 0 0 71000 0.0022 238000 152 0 0 71000 0.0018 3140000 126 0 0 71000 # #