#getFADs.f vers 1.5 starts... #
#Copyright (C) 2013 F.D.E. Committee #This data file is free software - you can redistribute it and/or #modify it under the terms of the GNU General Public License as #published by the Free Software Foundation; either version 2 of the #license, or (at your option) any later version. #This data file is distributed in the hope that it will be useful, #but WITHOUT ANY WARRANTY - without even the implied warranty of #MERCHANTABILITY or FITNESS FOR A PARTICULAR PURPOSE. See the #GNU General PUblic License for more details. #You should have received a copy of the GNU General PUblic License #along with this program - if not, write to the Free Software #Foundation, Inc., 59 Temple Place - Suite 330, Boston, MA 02111-1307, USA #Try also their web site: http://www.gnu.org/copyleft/gpl.html # A36 Steel Hot Rolled # Machined from 5/8 inch hot rolled plate. # Ref.: R.J.Mattos, F.V.Lawrence, "Estimation of the Fatigue Crack Initiation # Life in Welds Using Low Cycle Fatigue Concepts," Fracture Control Rep.19 # Univ. of Illinois, Oct. 1975. # NOTE!: For BS7910 FADs required Tags are: # #FileType= #DataType= #Sy= #Su= #E= # #Stress_units= #Strain_units= # #FileType= strain_stress #DataType= engineering #Can be "engineering" or "true" #NAME= ASTM-A36 #NAME= HotRolled #NAME= Steel #Stress_units= mpa #Strain_units= strain #Sy= 224. mpa = 32.5 ksi #Su= 414. mpa = 60.0 ksi #eu= 0.14 #strain at Su # Found EMOD = 190000.00 #E= 190000 mpa 27500 ksi #FractureStrain= 1.19 #FractureStress= 952 mpa = 138 ksi #monotonic_K= 780 mpa, 113 ksi #monotonic_n= 0.258 #BHN= 0. not reported #%RA= 69.7 % #From initial MattosStress-Strain plot # 0.00371 229 # 0.00474 230 # 0.00647 229 # 0.00750 230 # 0.00956 230 # 0.01121 232 # 0.01253 238 # 0.01367 243 # 0.01470 252 # 0.01608 264 #From Mattos Stress vs Plastic strain #(converted back to Engr.SS) #EngrStr EngrSts_mpa #