#Name= SAE945X ColdRolled 61%   R=-1  da/dn data
# 4.83mm hot rolled plate Cold Rolled to 61% reduction in thickness
# Chem.: .05Cwt% .45Mn .008S .011Nb
# Ref.: M.T.Yu, D.L.DuQuesnay, T.H.Topper, "Fatigue Bhehavior
#      of Cold-Rolled SAE Grade 945X HSLA Steel," ASTM
#     JTest.Eval. V18 N4 July 1990 pp.274-280.
# Note: Points digitized from graph to exhibit spread of data.
# Original data "K" is tensile portion only. Thus factor 2.0 applied

# convert2MPa_mm  vers. 1.4 starts...
# Program convert to table of mpa_mm, from other units table
#Got Original #deltaKunits=                     mpa_m     
#Got Original #dadnunits=                     mm        
#Conversions:
## 1 ksi*sqrt(inch) = 1.0989*MPa*sqrt(m)
## 1 MPa*sqrt(m)  =   31.6228*N/(mm**(3/2) )
## 1 MPa*sqrt(mm) =         1 N/(mm**(3/2) )
#All inputs converted to    MPa*sqrt(mm)   and  mm/cycle
#Note that this is same as  N/(mm**(3/2))  and  mm/cycle
#deltaKunits=  mpa_mm
#dadnUnits= mm

#   MPa*sqrt(mm)  mm/Cycle
332.325 0.1123850E-07
342.689 0.1157950E-07
349.111 0.3617220E-08
377.328 0.2377490E-06
380.492 0.5666080E-08
386.262 0.4609350E-06
398.525 0.1616100E-06
407.18 0.4753160E-06
425.122 0.3285750E-07
428.609 0.6724020E-06
464.17 0.6186890E-06
469.602 0.8739250E-06
490.853 0.8384320E-06
491.915 0.1366900E-05
540.066 0.1137910E-05
578.711 0.1542830E-05
594.607 0.1337630E-05
660.056 0.1790110E-05
663.541 0.1485310E-05
710.552 0.2325080E-05
714.441 0.1847790E-05
778.509 0.3021920E-05
814.439 0.2405150E-05
830.111 0.4595690E-05
899.694 0.3558780E-05
945.61 0.7006380E-05
1049.14 0.1051880E-04
1386.08 0.8691700E-05