#Name= SAE945X   Cold Rolled 30%  R=-1 da/dN data
# 4.83mm hot rolled plate Cold Rolled to 30% reduction in thickness
# Chem.: .05Cwt% .45Mn .008S .011Nb
# Ref.: M.T.Yu, D.L.DuQuesnay, T.H.Topper, "Fatigue Bhehavior
#      of Cold-Rolled SAE Grade 945X HSLA Steel," ASTM
#     JTest.Eval. V18 N4 July 1990 pp.274-280.
# Note: Points digitized from graph to exhibit spread of data.
# Original data "K" is tensile portion only. Thus factor 2.0 applied

# convert2MPa_mm  vers. 1.4 starts...
# Program convert to table of mpa_mm, from other units table
#Got Original #deltaKunits=                     mpa_m     
#Got Original #dadnunits=                     mm        
#Conversions:
## 1 ksi*sqrt(inch) = 1.0989*MPa*sqrt(m)
## 1 MPa*sqrt(m)  =   31.6228*N/(mm**(3/2) )
## 1 MPa*sqrt(mm) =         1 N/(mm**(3/2) )
#All inputs converted to    MPa*sqrt(mm)   and  mm/cycle
#Note that this is same as  N/(mm**(3/2))  and  mm/cycle
#deltaKunits=  mpa_mm
#dadnUnits= mm

#   MPa*sqrt(mm)  mm/Cycle
347.147 0.1015920E-06
352.561 0.2557710E-06
369.36 0.3822650E-06
378.918 0.4370260E-06
382.253 0.4008360E-08
405.589 0.6628710E-06
432.503 0.7576410E-06
444.355 0.3910160E-07
446.153 0.4497650E-06
448.188 0.3933310E-06
451.682 0.6148730E-06
461.306 0.7686890E-06
479.521 0.7571350E-06
488.166 0.5295220E-06
498.497 0.7131670E-06
513.316 0.1098220E-05
536.362 0.6716030E-06
554.439 0.1312480E-05
566.662 0.1113990E-05
581.859 0.7790520E-06
589.791 0.5530410E-06
614.303 0.1875190E-05
625.307 0.1391960E-05
652.6 0.1615070E-05
675.533 0.1498830E-05
689.908 0.1901900E-05
732.612 0.2048140E-05
741.732 0.2717830E-05
817.93 0.4928100E-05
854.271 0.3824690E-05
958.74 0.5629220E-05
999.976 0.9063920E-05
1128.2 0.7920680E-05
1344.51 0.1274250E-04
1489.85 0.1715270E-04
1582.07 0.1847170E-04
1735.27 0.5898940E-04
1790.34 0.3202470E-04