#Name= SAE945X HotRolled  R=-1 dadn data
#hot rolled 4.83mm plate, mechanically Capped, pickled
# Chem.: .05Cwt% .45Mn .008S .011Nb
# Ref.: M.T.Yu, D.L.DuQuesnay, T.H.Topper, "Fatigue Bhehavior
#      of Cold-Rolled SAE Grade 945X HSLA Steel," ASTM
#     JTest.Eval. V18 N4 July 1990 pp.274-280.
# Note: Points digitized from graph to exhibit spread of data.
# Original data "K" is tensile portion only. Thus factor 2.0 applied

#convert2MPa_mm  vers. 1.4 starts...
#Program convert to table of mpa_mm, from other units table
#Got Original #deltaKunits=                     mpa_m     
#Got Original #dadnunits=                     mm        
#Conversions:
## 1 ksi*sqrt(inch) = 1.0989*MPa*sqrt(m)
## 1 MPa*sqrt(m)  =   31.6228*N/(mm**(3/2) )
## 1 MPa*sqrt(mm) =         1 N/(mm**(3/2) )
#All inputs converted to    MPa*sqrt(mm)   and  mm/cycle
#Note that this is same as  N/(mm**(3/2))  and  mm/cycle

#deltaKunits=  mpa_mm
#dadnUnits= mm
#   MPa*sqrt(mm)  mm/Cycle
372.611 0.6649320E-06
407.403 0.7324010E-07
420.273 0.6256970E-06
434.851 0.3297470E-06
434.935 0.4992990E-06
452.317 0.1416330E-05
459.573 0.9051900E-07
461.837 0.3373970E-06
470.01 0.7034270E-06
490.731 0.9568110E-06
509.999 0.6391140E-06
519.085 0.1709090E-05
532.792 0.3018030E-05
560.592 0.6233820E-06
585.595 0.2435180E-05
590.424 0.1062000E-05
635.176 0.9765170E-06
674.679 0.1312330E-05
732.213 0.1763140E-05
771.154 0.2797490E-05
836.897 0.3627160E-05
912.311 0.6553680E-05
1079.11 0.1038290E-04