#getFADs.f   vers 0.5 starts...
# API X100 pipeline steel,
# from 914mm OD 143mm WT pipe, longitudinal direction
# Chem.: .07C wt% .2Si 2.0Mn .01P .001Si .02Nb Other: Cu,Ni,Mo,Ti
# Bainitic microstructure with finely dispersed Martensite-Austenite 2nd phase.
# Ref.: Okatsu, M., N.Shikanai, J.Kondo, "Development of a High-Deformability
# Linepipe with Resistance to Strain-aged Hardening by HOP (Heat-treatment
# On-line Process), JFE Tech. Report No. 12, Oct 2008.
#
#NOTE!: For BS7910 FADs required Tags are: #FileType= #DataType= #Sy= #Su= #E=
##Stress_units= #Strain_units=
#
#FileType= strain_stress
#DataType= engineering     #Can be "engineering" or "true"
#NAME= API_X100
#NAME= PipeSteel
#Stress_units= mpa
#Strain_units= strain
#Sy= 658. mpa
#Su= 822. mpa  Ultimate
#eu= 0.065 #strain at Su
 # Found EMOD =   200000.00    
#E= 200000 mpa  29000 ksi observed from graph
#BHN= 0. not reported
#%RA=  0.0 % not reported
#EngRStr EngrSts TrueStr TrueSts_mpa
 #CHECK THESE Inputs:
 #Stress_units=mpa        Strain_units=strain    
 #EMOD=   200000.00      Sult=   822.00000      Syield=   658.00000    
# Checking for Upper Yld: Strain at yield=  0.00529 Syield=    658.0
#Lrmax=  1.12 < 1.20 indicates an  HSLA type material. No Lueders check needed.
#FADinput #E=  200000. mpa
#FADinput #Sy=  658. mpa
#FADinput #Su=   822. mpa
#FADinput TrueStrain TrueStress_mpa
#FADinput  0.00000    0.0
#FADinput  0.00173  392.7
#FADinput  0.00210  470.0
#FADinput  0.00287  512.5
#FADinput  0.00312  548.7
#FADinput  0.00375  592.2
#FADinput  0.00426  610.6
#FADinput  0.00478  633.0
#FADinput  0.00504  646.2
#FADinput  0.00554  662.7
#FADinput  0.00619  686.2
#FADinput  0.00684  699.8
#FADinput  0.00748  713.3
#FADinput  0.00799  723.8
#FADinput  0.00877  733.4
#FADinput  0.00980  746.3
#FADinput  0.01199  764.1
#FADinput  0.01482  780.5
#FADinput  0.01917  797.1
#FADinput  0.02289  809.3
#FADinput  0.02810  821.8
#FADinput  0.03329  832.2
#FADinput  0.03581  838.5
#FADinput  0.04046  846.6
#FADinput  0.04783  856.0
#FADinput  0.06792  879.8
#FADinput  0.07884  882.9
#FADinput  0.08689  886.8
#FADinput  0.09190  890.2
#FADinput  0.09938  893.5
#FADinput  0.10469  893.8
#FADinput  0.10903  893.3
#FADinput  0.11266  894.3
#FAD1= 1
#Krmax= 0.707   #FAD1
#Srmax= 0.8     #FAD1
0.0 0.707       #FAD1
0.8 0.707       #FAD1
0.8 0.0         #FAD1

   0.0000000       1.0000000            #FAD2a
  4.68591712E-02  0.99969262            #FAD2a
  9.37183425E-02  0.99877006            #FAD2a
  0.14057751      0.99722981            #FAD2a
  0.18743668      0.99506181            #FAD2a
  0.23429586      0.99224007            #FAD2a
  0.28115502      0.98871106            #FAD2a
  0.32801419      0.98437899            #FAD2a
  0.37487337      0.97908902            #FAD2a
  0.42173254      0.97260821            #FAD2a
  0.46859172      0.96460611            #FAD2a
  0.51545089      0.95463711            #FAD2a
  0.56231004      0.94212645            #FAD2a
  0.60916919      0.92636698            #FAD2a
  0.65602833      0.90653116            #FAD2a
  0.70288748      0.88170952            #FAD2a
  0.74974662      0.85098428            #FAD2a
  0.79660577      0.81354815            #FAD2a
  0.84346491      0.76887220            #FAD2a
  0.89032406      0.71691412            #FAD2a
  0.93718320      0.65833789            #FAD2a
  0.98404235      0.59468907            #FAD2a
   1.0309016      0.52844548            #FAD2a
   1.0777607      0.46285719            #FAD2a
   1.0777607      0.0           #FAD2a

#FAD2b=       33      #FAD2b
   0.0000000       1.0000000            #FAD2b
  0.59677529      0.96108449            #FAD2b
  0.71426278      0.92118001            #FAD2b
  0.77882457      0.84830552            #FAD2b
  0.83390069      0.83285546            #FAD2b
  0.90002793      0.79380530            #FAD2b
  0.92795765      0.76603287            #FAD2b
  0.96203297      0.74201101            #FAD2b
  0.98213851      0.73160523            #FAD2b
   1.0070882      0.71130234            #FAD2b
   1.0429107      0.68913370            #FAD2b
   1.0634768      0.66765124            #FAD2b
   1.0840685      0.64849252            #FAD2b
   1.0999367      0.63481760            #FAD2b
   1.1145971      0.61410177            #FAD2b
   1.1246201      0.58845359            #FAD2b
   1.1246201      0.0           #FAD2b