#Dindinger and Cordes,  Double Lab Weld Specimen plate material
#Compact TensR=0.1  DeltaK_mpa-m  da/dn_m/cyc
# convert2MPa_mm  vers. 1.3 starts...
# Program convert to table of mpa_mm, from other units table
#Name= xxxSteel                           
#Got Original #deltaKunits=                     mpa_m     
#Got Original #dadnunits=                     meter     
#
#Conversions:
# 1 ksi*sqrt(inch) = 1.0989*MPa*sqrt(m)
# 1 MPa*sqrt(m)  =   31.6228*N/(mm**(3/2) )
# 1 MPa*sqrt(mm) =         1 N/(mm**(3/2) )

#All inputs converted to    MPa*sqrt(mm)   and  mm/cycle
#Note that this is same as  N/(mm**(3/2))  and  mm/cycle

#   MPa*sqrt(mm)  mm/Cycle
 0.1906855E+03  0.1539000E-05
 0.1935315E+03  0.1674000E-05
 0.1963776E+03  0.1812000E-05
 0.1989074E+03  0.1825000E-05
 0.2014372E+03  0.1908000E-05
 0.2042833E+03  0.2025000E-05
 0.2071293E+03  0.2080000E-05
 0.2099754E+03  0.2301000E-05
 0.2128215E+03  0.2507000E-05
 0.2159837E+03  0.2410000E-05
 0.2185135E+03  0.2436000E-05
 0.2213596E+03  0.2581000E-05
 0.2245219E+03  0.2569000E-05
 0.2276842E+03  0.2774000E-05
 0.2308465E+03  0.2916000E-05
 0.2340087E+03  0.3073000E-05
 0.2371710E+03  0.3299000E-05
 0.2400171E+03  0.3391000E-05
 0.2434956E+03  0.3345000E-05
 0.2466579E+03  0.3467000E-05
 0.2501364E+03  0.3721000E-05
 0.2532986E+03  0.4008000E-05
 0.2570934E+03  0.4094000E-05
 0.2605719E+03  0.4168000E-05
 0.2640504E+03  0.4422000E-05
 0.2675289E+03  0.4542000E-05
 0.2713236E+03  0.4613000E-05
 0.2748021E+03  0.4638000E-05
 0.2789131E+03  0.4854000E-05
 0.2820754E+03  0.5265000E-05
 0.2861863E+03  0.5626000E-05
 0.2899811E+03  0.5776000E-05
 0.2940920E+03  0.5814000E-05
 0.2978868E+03  0.6160000E-05
 0.3019977E+03  0.6421000E-05
 0.3061087E+03  0.6896000E-05
 0.3105359E+03  0.7450000E-05
 0.3146469E+03  0.7315000E-05
 0.3187578E+03  0.7186000E-05
 0.3228688E+03  0.7811000E-05
 0.3272960E+03  0.8556000E-05
 0.3317232E+03  0.8621000E-05
 0.3358341E+03  0.8737999E-05